| Colour | Brown |
|---|---|
| Consistency, NLGI No. | NLGI 2 |
| Penetration, Worked, 25 °C, 60 strokes | 288 0.1 mm |
| Kin. Viscosity Base Oil at 40 °C | 190 mm²/s |
| Dropping Point | 205 °C |
| Colour Visual | Dark grey |
|---|---|
| Consistency | NLGI 2 |
| Penetration, Worked, 25 °C, 60 strokes | 286 0.1 mm |
| Kin. Viscosity Base Oil at 40 °C | 110 mm²/s |
| Dropping Point | 190 °C |
| Colour Visual | Blue |
|---|---|
| Consistency | NLGI 2 |
| Penetration, Worked, 25 °C, 60 strokes | 280 0.1 mm |
| Kin. Viscosity Base Oil at 40 °C | 210 mm²/s |
| Dropping Point | 300 °C |
| Appearance | Amber to Brown |
|---|---|
| Thickener type | Lithium |
| Base oil | Mineral oil |
| Consistency | 2 |
| Worked Penetration (60 strokes @ 25°C / 77°F) | 265-295 |
| Consistency | NLGI 00 |
|---|---|
| Penetration, Worked, 25 °C, 60 strokes | 420 0.1 mm |
| Kin. Viscosity Base Oil at 40 °C | 120 mm²/s |
| Dropping Point | 170 °C |
| Four Ball Test, Weld Load | 2800 N |
| NLGI Consistency | 2 |
|---|---|
| Soap Type | Lithium |
| Base Oil | Mineral |
| Kinematic Viscosity@40°C | 220 cSt |
| Kinematic Viscosity@100°C | 19 cSt |
| NLGI Consistency | 2 |
|---|---|
| Color | Red |
| Soap Type | Lithium complex |
| Base Oil Type | Mineral |
| Base Oil Viscosity @40℃ | 220 cSt |
| NLGI Consistency | 2 |
|---|---|
| Colour | Black |
| Soap Type | Lithium/Calcium |
| Base Oil | Mineral |
| Kinematic Viscosity @40℃ | 220 cSt |
| Weight (Kg) | 12.5 |
|---|---|
| Colour | Brown |
| Consistency, NLGI No. | NLGI 2 |
| Penetration, Worked, 25 °C, 60 strokes | 288 0.1 mm |
| Kin. Viscosity Base Oil at 40 °C | 190 mm²/s |
| NLGI Consistency | 2 |
|---|---|
| Soap Type | Lithium |
| Base Oil | Mineral |
| Kinematic Viscosity@40°C | 220 cSt |
| Kinematic Viscosity@100°C | 19 cSt |
| Colour Visual | Dark grey |
|---|---|
| Consistency | NLGI 2 |
| Penetration, Worked, 25 °C, 60 strokes | 286 0.1 mm |
| Kin. Viscosity Base Oil at 40 °C | 110mm²/s |
| Dropping Point | 190°C |